3003 h16 diamond embossed aluminum coil
The 3003 H16 diamond embossed aluminum coil is a popular choice in the aluminum alloy industry, known for its excellent combination of strength, corrosion resistance, and aesthetic appeal. The unique diamond embossing pattern provides enhanced slip resistance, which makes it ideal for both functional and decorative applications. Manufactured from high-quality 3003 aluminum alloy and processed under the H16 temper designation, this embossed aluminum coil offers excellent workability along with good structural integrity.
Chemical Composition of 3003 Aluminum Alloy
| Element | % Composition (Typical) |
|---|---|
| Aluminum | Balance (≥ 97.0%) |
| Manganese (Mn) | 1.0 - 1.5 |
| Copper (Cu) | 0.05 - 0.20 |
| Iron (Fe) | ≤ 0.7 |
| Silicon (Si) | ≤ 0.6 |
| Zinc (Zn) | ≤ 0.1 |
| Magnesium (Mg) | ≤ 0.1 |
| Other Elements | Each ≤ 0.05, Total ≤ 0.15 |
Note: Actual alloy compositions may slightly vary depending on production allowances.
Mechanical Properties of 3003 H16 Aluminum Coil
| Property | Value | Test Method/Standard |
|---|---|---|
| Ultimate Tensile Strength (MPa) | 160 - 210 | ASTM B908 |
| Yield Strength (MPa) | ≥ 90 | ASTM B906 |
| Elongation (%) | 3 - 6 | ASTM E8 |
| Density (g/cm³) | 2.73 | ASTM B211 |
| Hardness (HB) | 41 | Brinell Hardness |
Temper H16 indicates that the aluminum coil is strain hardened and partially annealed, characterized by relatively high hardness and strength while maintaining good ductility.
Features of 3003 H16 Diamond Embossed Aluminum Coil
Excellent Corrosion Resistance:The presence of manganese provides enhanced corrosion resistance, especially against atmospheric conditions, making it suitable for outdoor and harsh environments.
Superior Strength and Durability:H16 temper results in higher tensile strength compared to softer alloys while retaining enough ductility to prevent cracking during forming or fabrication.
Anti-slip Surface with Decorative Pattern:The diamond embossing creates an attractive textured surface that reduces the risk of slipping, making this product safe and functional for flooring, walkways, and industrial platforms.
Good Workability:Despite being strain hardened, 3003 H16 maintains good formability, allowing it to be fabricated into different shapes and sizes.
Lightweight Yet Strong:The excellent strength-to-weight ratio of aluminum significantly reduces railing and support structure weight without sacrificing durability.
High Thermal and Electrical Conductivity:It retains good heat and electricity transmission properties suitable for various industrial applications.
Recyclable and Eco-friendly:Aluminum is 100% recyclable without loss of properties, making it a sustainable material choice.
Typical Specifications
| Parameter | Range |
|---|---|
| Coil Width | 500 mm to 1500 mm |
| Coil Thickness | 0.4 mm to 3.0 mm |
| Coil Weight | 1,000 Kg to 5,000 Kg |
| Surface Finish | Diamond Embossed Pattern |
| Coating | Optional anodizing or PVDF coating |
| Temper | H16 |
Applications of 3003 H16 Diamond Embossed Aluminum Coil
- Architectural and Building Industry:
- Elevator flooring and panels
- Stair treads and handrails
- Ceiling panels and wall cladding
- Decorative façades
- Transportation Industry:
- Flooring and panels in buses, trucks, and trailers
- Cargo containers and refrigerated trucks
- Industrial Flooring and Walkways:
- Factory floors, ramps, and platforms
- Safety walkways with slip-resistant surface
- Food and Chemical Processing Equipment:
- Non-toxic and corrosion-resistant surfaces for storage tanks
- Cover sheets and ventilation ducts
- Household Applications:
- Kitchen appliances and decorative surfaces
- Furniture components and panels
- Marine and Shipbuilding:
- Boat and ship flooring due to corrosion resistance and textured surface